Surface Modification on CoCrMo Alloy to Improve the Adhesion Strength of Hydroxyapatite Coating

Mas Ayu, Hassan and Izman, Sudin and R., Daud and Krishnamurithy, G. and A., Shah and Siti Haryani, Tomadi and Salwani, Mohd Salleh (2017) Surface Modification on CoCrMo Alloy to Improve the Adhesion Strength of Hydroxyapatite Coating. Procedia Engineering, 184. pp. 399-408. ISSN 1877-7058. (Published)

[img] PDF
Surface Modification on CoCrMo Alloy to Improve the Adhesion Strength of Hydroxyapatite Coating.pdf - Published Version
Restricted to Repository staff only

Download (1MB) | Request a copy
[img]
Preview
PDF
Surface Modification on CoCrMo Alloy to Improve the Adhesion Strength of Hydroxyapatite Coating 1.pdf - Published Version

Download (124kB) | Preview

Abstract

Surface modification is often required in order to improve the biological and tribological properties of metallic implants. In the present study, Co-Cr-Mo alloy was oxidized in atmospheric condition to create oxide interlayer (Cr2O3) prior to hydroxyapatite (HA) coating. The effect of oxide interlayer on the adhesion strength of HA coating on oxidized Co-Cr-Mo substrate was investigated. The surface of oxide interlayer was rough and contained abundant of pores, which helps in providing better mechanical interlocking to HA coating. Scanning electron microscopy and X-ray diffraction techniques were used to characterize the surface morphology of the HA coating whilst a Revetest scratch test was used to measure the adhesion strength of HA coating on oxidized substrates. The oxide interlayer on the substrate was able to prevent severe cracks while maintaining the porosity of the coated layer. Scratch test results showed that adhesion strength of the HA coating on substrates with interlayer was significantly higher than those without interlayer (1.40 N Vs 1.04 N; p<0.05). Increasing sintering temperature increases adhesion strength proportionally. These findings suggest that the porous oxide interlayer provides better anchorage whilst minimizing surface cracks of HA on Co-Cr-Mo substrates.

Item Type: Article
Uncontrolled Keywords: Co-Cr-Mo alloy; Thermal oxidation; Hydroxyapatite; Dip coating; Adhesion strength
Subjects: T Technology > TJ Mechanical engineering and machinery
Faculty/Division: Faculty of Mechanical Engineering
Depositing User: Mrs. Neng Sury Sulaiman
Date Deposited: 09 Aug 2017 01:53
Last Modified: 14 Aug 2017 02:20
URI: http://umpir.ump.edu.my/id/eprint/18042
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item