Experiment study on surface integrity in end milling of hastelloy C-2000 superalloy

Norhaida, Ab Razak and Rahman, Md Mustafizur and Kadirgama, Kumaran (2013) Experiment study on surface integrity in end milling of hastelloy C-2000 superalloy. International Journal of Automotive and Mechanical Engineering (IJAME), 9. pp. 1578-1587. ISSN 1985-9325(Print); 2180-1606 (Online). (Published)

[img]
Preview
Pdf (fkm-2013-mustafizur-ExperimentStudyOnSurface )
P179.pdf

Download (525kB)

Abstract

This paper presents an experimental study of surface integrity in end milling of Hastelloy C-2000. The experiment was carried out using two different cutting inserts under wet conditions –namely Physical Vapor Deposition (PVD) coated carbide with TiAlN and uncoated carbide. Design of experiment (DOE) was implemented with Box-Behnken design. The surface integrity of workpiece was analyzed through scanning electron microscope (SEM) and chemical element changes were inspected by energy dispersive X-ray (EDX) test. The surface integrity of Hastelloy C-2000 was better when machining with coated carbide compare to uncoated carbide cutting insert mainly due to coating layer of coated carbide which actedas protecting layer to the cutting tool insert. Surface defects such as feed marks, surface tearing, plucking, cracking and adhered chips were found during machining process. The chemical element changes happened due to the adhesion and diffusion mechanism which were identifyusing SEM and EDX.

Item Type: Article
Uncontrolled Keywords: Nickel based superalloy; Coated carbide; End mill; Uncoated carbide; Adhesion wear; Diffusion wear
Subjects: T Technology > TJ Mechanical engineering and machinery
Faculty/Division: Faculty of Mechanical Engineering
Depositing User: azimah
Date Deposited: 24 Mar 2014 08:11
Last Modified: 22 Aug 2023 03:22
URI: http://umpir.ump.edu.my/id/eprint/3991
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item