Effect of Clay as a Nanomaterial on Corrosion Potential of Steel Reinforcement Embedded in Ultra-High Performance Concrete

Mohd Faizal, Md Jaafar and Hamidah, M. S. and Muhd Nurhasri, M. S. and Noorli, I. (2016) Effect of Clay as a Nanomaterial on Corrosion Potential of Steel Reinforcement Embedded in Ultra-High Performance Concrete. In: InCIEC 2015: Proceedings of the International Civil and Infrastructure Engineering Conference. Springer, Singapore, pp. 679-687. ISBN 978-981-10-0154-3

[img]
Preview
PDF
Effect of Clay as a Nanomaterial on Corrosion Potential of Steel Reinforcement Embedded in Ultra-High Performance Concrete.pdf

Download (41kB) | Preview

Abstract

The effect of clay as nanomaterial or nanoclay (NC) on corrosion potential of steel reinforcement embedded in ultra-high performance concrete (UHPC) due to the early age properties of UHPC was investigated. In this present research, ordinary Portland cement (OPC) was partially replaced by NC at 1, 3, and 5 % by weight of cement to produce the nanoclayed UHPC. It is well recognized that the corrosion of steel reinforcement would affect the service life of the reinforced concrete structure performance. To overcome this problem, UHPC was benefited due to its superior characteristic in term of density and durability as compared to OPC concrete itself. In this present research, half-cell potential (HCP) was used to monitor and measure the corrosion potential of steel reinforcement embedded in UHPC and nanoclayed UHPC. Meanwhile, weight loss of corroded steel reinforcement and pH values of hardened UHPC and nanoclayed UHPC were also conducted as follows to the specific procedures. All the samples were immersed in 3 % sodium chloride solution up to 91 days of exposure. The results revealed that the corrosion activity of steel reinforcement embedded in UHPC with 5 % NC recorded the lowest corrosion potential readings compare to those UHPC. It is also shows that the pH value of concrete and weight loss of corroded steel reinforcement in UHPC alone is highest compared to UHPC incorporating different levels of NC. As regards to the results, it is revealed that replacing NC as a replacement to cement significantly enhanced the chloride penetration of nanoclayed UHPC. It is also indicated that the corrosion potential decreased with the increase of NC and as a result delayed the corrosion initiation.

Item Type: Book Chapter
Uncontrolled Keywords: Ultra-high performance concrete; Nanoclay; Nanoclayed UHPC; Corrosion potential; Weight loss; pH value
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Faculty/Division: Faculty of Civil Engineering & Earth Resources
Depositing User: Mrs. Neng Sury Sulaiman
Date Deposited: 11 Jan 2017 03:47
Last Modified: 03 May 2018 06:38
URI: http://umpir.ump.edu.my/id/eprint/14121
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item