Grain size effect on softening behaviour of Al-Mg alloy due to paint bake heat treatment

Nadarajah, Hemalatha (2007) Grain size effect on softening behaviour of Al-Mg alloy due to paint bake heat treatment. Faculty of Mechanical Engineering, Universiti Malaysia Pahang.

[img]
Preview
PDF
HEMALATHA__NADARAJAH.PDF

Download (742kB)

Abstract

Aluminium- Magnesium (Al-Mg) alloys have very good formability properties and have been used extensively for interior structural components of automotive Body in White (BIW). The alloys in an annealed temper achieve their strength through work hardening mechanism during press forming process. The strengthening mechanism is due to Mg atoms in solid solution exerting dislocation drag during low temperature plastic straining. However at elevated temperatures, high diffusivity of Mg atoms allows easy dislocations rearrangements which lead to reduction of mechanical strength. This phenomenon is called softening. Furthermore, accumulation of stored energy in the dislocations substructures due plastic straining during press forming process also serves as a large driving force for thermal recovery. These two factors contribute Al-Mg alloy sheet to be susceptible to softening during paint bake cycle. Al-Mg sheets for automotive Body in White (BIW) applications are normally supplied in an annealed condition known as "-0-" temper. The microstructure of an annealed sheet is characterized by equiaxed recrystallized grains. Average size of grains depends on actual rolling schedule and heat treatment stages on those particular sheets. This project investigates the effect of varying grain size on softening characteristics of pre-strained sheets after paint bake cycle. This is done by annealing Al-Mg H32 sheets in different temperatures to obtain different grain size. Smaller grain size would have more softening than larger grain size.

Item Type: Undergraduates Project Papers
Additional Information: Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2007, SV: DR. AHMAD SYAHRIZAN BIN SULAIMAN.
Uncontrolled Keywords: Aluminum -- magnesium alloys
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Faculty/Division: Faculty of Mechanical Engineering
Depositing User: Shamsor Masra Othman
Date Deposited: 14 Mar 2012 03:03
Last Modified: 31 May 2021 03:37
URI: http://umpir.ump.edu.my/id/eprint/2271
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item