Effect of copper based fillers composition the strength of brazed joint

Aiman, Mohd Halil and A. J. S., Hanifah (2018) Effect of copper based fillers composition the strength of brazed joint. In: Joining and Welding Symposium 2018 (JWS 2018), 23 October 2018 , Library, UMP Pekan. pp. 1-6.. (Unpublished)

32.1 Effect of copper based fillers composition.pdf

Download (7kB) | Preview


Vacuum brazing of copper-based filler was performed using pure copper plate as its based metal. The brazed joint were obtained at different temperatures, 680oC and 730oC, with same holding time, which is 30 minutes. MBF 2005 (Cu, 5.7wt.%Ni, 9.7wt.%Sn, 7.0wt.%P), MBF 2002 (Cu, 9.9wt.%Ni, 4.0wt.%Sn, 7.8wt.%P) and VZ 2250 (Cu, 7.0wt.%Ni, 9.3wt.%Sn, 6.3wt.%P) alloys were used as brazing filler materials. The intermetallic compound (IMC) and mechanical properties of the joints were investigated in detail. The result show that the typical interfacial microstructure of the brazed joints is Cu3P and (CuNi)2P. As the brazing temperature increase from 680oC to 730oC, the IMC will became more thick but decrease in joining strength due to brittle IMC formation occur during the heating process. The maximum shear strength reached 112 MPa at 680oC for MBF 2002 and 129 MPa at 730oC for MBF 2005. Hence, the proper in weight percentage composition in filler alloys also is the factor that give enhancement to the strength of brazed joint.

Item Type: Conference or Workshop Item (Lecture)
Uncontrolled Keywords: Intermetallic compound (IMC); Shear strength; Temperature; Copper-based filler
Subjects: T Technology > TJ Mechanical engineering and machinery
Faculty/Division: Faculty of Mechanical Engineering
Depositing User: Pn. Hazlinda Abd Rahman
Date Deposited: 12 Feb 2019 04:42
Last Modified: 12 Feb 2019 04:42
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item