Sonicated Sol-gel Preparation of Nanoparticulate ZnO Thin Films with Various Deposition Speeds: The highly Preferred c-axis (0 0 2) Orientation Enhances the Final Properties

Ayib Rosdi, Zainun and M. F., Malek and Mohd Hafizan, Mamat and Z., Khusaimi and M. Z., Sahdan and M. Z., Musa and A. B., Suriani and N. D., Md Sin and S. B., Abd Hamid and M., Rusop (2014) Sonicated Sol-gel Preparation of Nanoparticulate ZnO Thin Films with Various Deposition Speeds: The highly Preferred c-axis (0 0 2) Orientation Enhances the Final Properties. Journal of Alloys and Compounds, 582. pp. 12-21. ISSN 0925-8388 (print); 1873-4669 (online)

[img] PDF
Sonicated Sol-gel Preparation of Nanoparticulate ZnO Thin Films with Various Deposition Speeds- The highly Preferred c-axis (0 0 2) Orientation Enhances the Final Properties.pdf
Restricted to Repository staff only

Download (2MB) | Request a copy
[img]
Preview
PDF
Sonicated Sol–Gel Preparation Of Nanoparticulate Zno Thin Films With Various Deposition Speeds- The Highly Preferred C-Axis (0 0 2) Orientation Enhances The Final Properties.pdf - Published Version

Download (67kB) | Preview

Abstract

Zinc oxide (ZnO) thin films have been deposited onto glass substrates at various deposition speeds by a sonicated sol-gel dip-coating technique. This work studies the effects of deposition speed on the crystallisation behaviour and optical and electrical properties of the resulting films. X-ray diffraction (XRD) analysis showed that thin films were preferentially oriented along the (0 0 2) c-axis direction of the crystal. The transformation sequence of strain and stress effects in ZnO thin films has also been studied. The films deposited at a low deposition speed exhibited a large compressive stress of 0.78 GPa, which decreased to 0.43 GPa as the deposition speed increased to 40 mm/min. Interestingly, the enhancement in the crystallinity of these films led to a significant reduction in compressive stress. All films exhibited an average transmittance of greater than 90% in the visible region, with absorption edges at ∼380 nm. The photoluminescence (PL) measurements indicated that the intensity of the emission peaks varied significantly with deposition speed. The optical band gap energy (Eg) was evaluated as 3.276–3.289 eV, which increased with decreasing compressive stress along the c-axis. The energy band gap of the resulting ZnO films was found to be strongly influenced by the preferred c-axis (0 0 2) orientation.

Item Type: Article
Additional Information: Indexed by Scopus. IF: 2.407
Uncontrolled Keywords: ZnO; Thin films; Sol–gel processes; X-ray diffraction; Strain
Subjects: T Technology > TK Electrical engineering. Electronics Nuclear engineering
Faculty/Division: Faculty of Electrical & Electronic Engineering
Depositing User: Mrs. Neng Sury Sulaiman
Date Deposited: 28 Aug 2014 02:59
Last Modified: 15 Jan 2018 07:41
URI: http://umpir.ump.edu.my/id/eprint/6444
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item