Creating Oxide Interlayer Through Thermal Oxidation Improves Adhesion Strength Of Hydroxyapatite Coating on Co-Cr-Mo Substrates

Mas Ayu, Hassan and Sudin, Izman and Mohammed Rafiq, Abdul Kadir and R., Daud and Mohd Faiz, Mohd Yusoff and Mahmood, Anwar and A., Shah (2015) Creating Oxide Interlayer Through Thermal Oxidation Improves Adhesion Strength Of Hydroxyapatite Coating on Co-Cr-Mo Substrates. In: 1st International Conference on Materials and Manufacturing Engineering and Technology, 28-31 July 2015 , Seoul, Korea. . (Unpublished)

[img]
Preview
PDF
Creating oxide interlayer through thermal oxidation improves adhesion strength of hydroxyapatite coating on Co-Cr-Mo substrates.pdf

Download (67kB) | Preview

Abstract

Improvements to the adhesion strength of hydroxyapatite (HA) coat by creating an oxide interlayer on cobalt-chromium-molybdenum (Co-Cr-Mo) substrate was assessed in this study. The amorphous HA films were crystallized by sintering HA at temperatures ranging from 550°C to 750°C for 1 hour. SEM and X-ray diffraction techniques were used to characterize the surface morphology of the HA coating whilst a Revetest scratch test was used to measure the adhesion strength of HA. The oxide interlayer on the substrate was able to prevent severe cracks while maintaining the porosity of the coated layer. Scratch test results showed that adhesion strength of the HA coatings on substrates with interlayer was significantly higher than those without interlayer (1.35 N Vs 1.04 N; p<0.05). Increasing sintering temperature increases adhesion strength proportionally. These findings suggest that the porosity of oxide interlayer provides better anchorage whilst minimizing surface cracks of HA on Co-Cr-Mo substrates.

Item Type: Conference or Workshop Item (Speech)
Uncontrolled Keywords: Biomaterial, Co-Cr-Mo alloy, oxide interlayer, HA, adhesion strength.
Subjects: T Technology > TJ Mechanical engineering and machinery
Faculty/Division: Faculty of Mechanical Engineering
Depositing User: Mrs. Neng Sury Sulaiman
Date Deposited: 20 Nov 2015 03:18
Last Modified: 31 Jan 2018 03:58
URI: http://umpir.ump.edu.my/id/eprint/11235
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item