Iqbal, AKM Asif and Arai, Yoshio (2016) Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy. In: 17th European Conference on Composite Materials (ECCM17) , 26-30 June 2016 , Munich, Germany. pp. 1-8.. (Unpublished)
![[img]](http://umpir.ump.edu.my/style/images/fileicons/application_pdf.png) |
PDF
Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy.pdf Restricted to Repository staff only Download (524kB) | Request a copy |
|
|
PDF
fkp-2016-asif-Stress Measurement During Crack Propagation.pdf Download (43kB) | Preview |
Abstract
The measurement of stress in the SiC particles during crack propagation was investigated by micro raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results showed that cracks due to monotonic loading propagated by the debonding of the particle/matrix interface and particle fracture. A high decrease in stress was observed with the interfacial debonding at the interface and with the particle fracture on the particle. Moreover, the critical tensile stresses for particle-matrix interface debonding and particle fracture developed in hybrid MMC were also estimated during the crack propagation.
| Item Type: | Conference or Workshop Item (Lecture) |
|---|---|
| Uncontrolled Keywords: | Cast Metal Matrix Composite (MMC), Crack propagation, Stress measurement, Raman spectroscopy |
| Subjects: | T Technology > TS Manufactures |
| Faculty/Division: | Faculty of Manufacturing Engineering |
| Depositing User: | Mrs. Neng Sury Sulaiman |
| Date Deposited: | 05 Oct 2016 01:51 |
| Last Modified: | 23 Feb 2018 03:35 |
| URI: | http://umpir.ump.edu.my/id/eprint/14055 |
| Download Statistic: | View Download Statistics |
Actions (login required)
 |
View Item |