Keong, Stephanie Wei San (2016) Effect of nonmagnetic PbO nanoparticles addition on the microstructure and electrical transport properties of YBa2Cu3O7. Faculty of Industrial Sciences and Technology, Universiti Malaysia Pahang.
|
Pdf
Effect of nonmagnetic PbO nanoparticles addition on the microstructure and electrical transport properties of YBa2Cu3O7.pdf Download (2MB) | Preview |
Abstract
Superconductors are materials that show zero resistance when subjected to temperature under its critical temperature. Yttrium Barium Copper Oxide (YBCO) was prepared using solid state reaction method by grinding, sintering and finally pressing the samples into pellets. The objective of the research ws to study the change in (i) microstructure and (ii) electrical transport properties of YBCO with the addition of 0.00 wt%, 0.01 wt%, 0.02 wt%, 0.03 wt% and 0.04 wt% nonmagnetic PbO nanoparticles, as well as to develop a laboratory scale method in determining the electrical properties of YBCO at liquid nitrogen temperature. The presence of superconductivity was tested and confirmed when the samples was allowed to levitate above a row of Neodymium magnet and the sample with 0.04 wt% PbO nanoparticle showed the longest levitation time. From the results obtained from the X-ray diffraction, it was noted that there was minimal changes to the microstructure and composition of the superconductor when the PbO nanoparticle was added to them. A four point probe was developed to test the critical temperature of the YBCO superconductor. The results obtained does not fulfil the expected results as the critical temperature obtained for the added sample is lower than that of the referenced results which is 90 K.
| Item Type: | Undergraduates Project Papers |
|---|---|
| Additional Information: | Project Paper (Bachelor of Applied Science (Honor) Material Technology) -- Universiti Malaysia Pahang – 2017, SV: DR. MUHAMMAD HAFIZ BIN MAZWIR, NO. CD: 10881 |
| Uncontrolled Keywords: | Nonmagnetic PbO; electrical transport |
| Subjects: | Q Science > Q Science (General) T Technology > TK Electrical engineering. Electronics Nuclear engineering |
| Faculty/Division: | Faculty of Industrial Sciences And Technology |
| Depositing User: | Mrs. Sufarini Mohd Sudin |
| Date Deposited: | 12 Mar 2018 03:03 |
| Last Modified: | 03 Oct 2023 06:45 |
| URI: | http://umpir.ump.edu.my/id/eprint/20078 |
| Download Statistic: | View Download Statistics |
Actions (login required)
 |
View Item |