Copper (II) oxide nanoparticles as additve in engine oil to increase the durability of piston-liner contact

Asnida, M. and Sakinah, Hisham and N. W., Awang and Amirruddin, Abdul Kadir and M. M., Noor and K., Kadirgama and D., Ramasamy and G., Najafi and F., Tarlochan (2018) Copper (II) oxide nanoparticles as additve in engine oil to increase the durability of piston-liner contact. Fuel, 212. pp. 656-667. ISSN 0016-2361

[img]
Preview
Pdf
Copper (II) oxide nanoparticles as additve in engine1.pdf

Download (56kB) | Preview

Abstract

In the current decade, the development of recyclable, renewable, and sustainable products to replace fossil products is an essential and important matter for industrial and environmental purposes. In the present study copper (II) oxide nanoparticles were dispersed in SAE10W-30 to reduce wear and friction on piston skirt. Moisture content and viscosity values were analysed to study the physical properties of the dispersed lubricant. The wear and friction performance was evaluated using a piston skirt-liner contact tester, and the material used was aluminium 6061, which is the standard material for piston skirt. The design of experiment (DOE) was constructed using the response surface methodology (RSM) technique. The influence of different operating parameters such as rotational speed (200 rpm, 250 rpm, 300 rpm), volume concentration (0.005% and 0.01% of dispersed nanomaterial), and load (2 N, 5.5 N, and 9 N) were determined and optimal lubricant concentration was obtained. FESEM was used to identify the type of wear occurring during the experimental process. The results showed that CuO nano-particles dispersed in the base oil exhibited good friction-reduction and anti-wear properties. The coefficient of friction obtained was 0.06125 and the wear rate was 0.2482 mm3/Nm when a concentration of 0.005% was used. SEM results showed that the constituent element of the nano-particles precipitated at the contact area. A protection layer was observed during the EDAX analysis. The optimal parameters obtained were 0.008% concentration; 291 rpm speed and 75.152 N load.

Item Type: Article
Additional Information: Indexed by Scopus
Uncontrolled Keywords: Nanoparticle; Copper (II) oxide; Engine oil; Durability
Subjects: T Technology > TJ Mechanical engineering and machinery
Faculty/Division: Centre of Excellence: Automotive Engineering Centre
Faculty of Mechanical Engineering
Depositing User: Mrs. Neng Sury Sulaiman
Date Deposited: 01 Aug 2018 02:38
Last Modified: 09 Jan 2019 07:27
URI: http://umpir.ump.edu.my/id/eprint/20412
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item