P84 Co-Polyimide-based Tubular Carbon Membrane: Effect of Pyrolysis Temperature

Norazlianie, Sazali and W. N. W., Salleh and N., Arsat and Z., Harun and K., Kadirgama (2019) P84 Co-Polyimide-based Tubular Carbon Membrane: Effect of Pyrolysis Temperature. Journal of Applied Membrane Science & Technology, 23 (1). pp. 17-24. ISSN 2600-9226

[img]
Preview
Pdf (P84 Co-Polyimide-based Tubular Carbon Membrane: Effect of Pyrolysis Temperature)
JAMST 3.pdf - Published Version

Download (1MB) | Preview

Abstract

In this study, the effect of carbonization temperature on the performance of carbon membrane was being investigated. P84 co-polyimide-based tubular carbon membrane were fabricated through the dip-coating technique. The prepared membranes were characterized by using the thermogravimetric analysis and scanning electron microscopy. CO2, N2, and CH4 pure gas were utilized in determination of the carbon membrane’s permeation attributes. In order to enhance the membrane’s performance, carbonization process was performed in Ar environment; with the flow rate of 200 ml/min. The carbonization process was done at various temperature, namely 600 oC, 700 oC, 800 oC and 900 oC in a constant heating rate of 3 oC/min. The increased in the temperature of carbonization leads to the production of small pores size carbon membrane. Carbon membrane prepared at 800 oC showed the highest CO2/CH4 and CO2/N2 selectivity of 63.2±5.2 and 61.3±1.7, respectively.

Item Type: Article
Uncontrolled Keywords: Tubular carbon membrane, carbonization process, gas separation, P84 co-polyimide
Subjects: T Technology > TP Chemical technology
Faculty/Division: Faculty of Mechanical Engineering
Depositing User: Dr. Norazlianie Sazali
Date Deposited: 18 Jan 2019 03:19
Last Modified: 18 Jan 2019 03:19
URI: http://umpir.ump.edu.my/id/eprint/23823
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item