Effect of graphite on mechanical, thermal and morphological properties of kenaf recycle polypropylene wood plastic composites

Ros Azlinawati, Ramli and Muhammad Syafiq, Zulkifli and Nurul Ekmi, Rabat (2020) Effect of graphite on mechanical, thermal and morphological properties of kenaf recycle polypropylene wood plastic composites. In: Symposium on Industrial Science and Technology, SISTEC 2019 , 22-23 Aug. 2019 , Kuantan, Malaysia. pp. 144-149., 981. ISSN 1662-9752

Preview	Pdf 6.1 Effect of graphite on mechanical, thermal and morphological properties of kenaf recycle.pdf Download (137kB) | Preview
	Pdf Effect of graphite on mechanical, thermal and morphological properties of kenaf recycle polypropylene wood plastic composites.pdf Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

The objective of this research is to investigate the effect of incorporating graphite filler on mechanical, thermal and morphological properties of wood recycled plastic composites (WrPC). WrPC was prepared using recycled polypropylene (rPP), kenaf core, maleic anhydride polypropylene (MAPP) and graphite filler. The graphite content in WrPC is 3 phr. All materials were premixed manually and fed into a single screw extruder and compression molded to prepare mechanical test specimens. The effect of graphite on tensile properties, impact strength, glass transition temperature (Tg) and morphological properties of WrPC were studied. Tensile strength was increased from 6.81 MPa to 10.07 MPa due to stronger interfacial adhesion between graphite and kenaf/rPP. However, the tensile modulus decreased significantly with the incorporation of graphite. Impact strength of WrPC was increased from 2.48 kJ/m2 to 2.83 kJ/m2 due to the present of graphite that gave effective distribution of applied stress and increase resistance of crack propagation. DSC results indicated that Tg of graphite/WrPC is comparable to WPC at 163°C. The internal structure of WrPC showed the addition of graphite had filled the voids and lead to smooth morphology.

Item Type:	Conference or Workshop Item (Lecture)
Uncontrolled Keywords:	Composites; Graphite; Kenaf; Recycle PP
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Faculty/Division:	Faculty of Industrial Sciences And Technology
Depositing User:	Pn. Hazlinda Abd Rahman
Date Deposited:	26 Feb 2021 02:55
Last Modified:	26 Feb 2021 02:55
URI:	http://umpir.ump.edu.my/id/eprint/30488
Download Statistic:	View Download Statistics

Actions (login required)

View Item