Microstructural and mechanical characterization of AlSi10Mg additively manufactured material using direct metal laser sintering technique

Tan, S. P. and M. A., Ramlan and M. S., Shaari and Takahashi, A. and Mohd Akramin, Mohd Romlay (2023) Microstructural and mechanical characterization of AlSi10Mg additively manufactured material using direct metal laser sintering technique. In: Lecture Notes in Mechanical Engineering; 6th International Conference in Mechanical Engineering Research, ICMER 2021 , 26 - 27 October 2021 , Virtual, Online. 349 -360.. ISSN 2195-4356 ISBN 978-981191456-0

Preview	Pdf Microstructural and mechanical characterization of AlSi10Mg.pdf Download (104kB) | Preview
	Pdf Microstructural and mechanical characterization of AlSi10Mg_FULL.pdf Restricted to Repository staff only Download (502kB) | Request a copy

Abstract

AlSi10Mg alloy produced by additive manufacturing (AM) technology using direct metal laser sintering (DMLS) technique has resulted better in handling complex geometry. However, limited studies are performed for this AM method to show the integrity of aluminium alloys produced by DMLS to meet the required industry standard. This study investigates the effect of post-process on microstructure, mechanical properties, and fatigue life behaviour to AlSi10Mg material that DMLS produces. In this study, the specimens were tested with different post-process types: annealing (TS) and heat treatment processes (T5 and T6 conditions). All test results were compared with as-built processed specimens. Scanning electron microscope (SEM) and optical microscope are used to capture the microstructure images. The results showed that the tensile strength of the post-processed was decreased approximately 25% (decreased from 391 to 299 MPa). Still, the ductility was approximately 200% (in-creased from 3.2 to 6.8%) higher than the as-built specimen. This is because spherical silicon particles become coarsened when the specimen ductility is increased after heat treatment. For fatigue behaviour, it shows the as-built and heat-treated specimens are closely similar compared to findings from the literature. Overall, this study showed that the post-process changed the tensile strength and microstructural of AlSi10Mg but only significantly improved fatigue performance.

Item Type:	Conference or Workshop Item (Lecture)
Additional Information:	Indexed by Scopus
Uncontrolled Keywords:	Additive manufacturing; AlSi10Mg; DMLS; Fatigue life; Mechanical characterization
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TL Motor vehicles. Aeronautics. Astronautics
Faculty/Division:	Institute of Postgraduate Studies Faculty of Mechanical and Automotive Engineering Technology
Depositing User:	Mrs Norsaini Abdul Samat
Date Deposited:	27 Nov 2023 01:51
Last Modified:	27 Nov 2023 01:51
URI:	http://umpir.ump.edu.my/id/eprint/39393
Download Statistic:	View Download Statistics

Actions (login required)

View Item