Fadzidah, Mohd Idris and Khamirul, Amin Matori and Ismayadi, Ismail and Idza Riati, Ibrahim and Rodziah, Nazlan and Farah Nabilah, Shafiee and Mohd Shamsul Ezzad, Shafie (2022) Materials’ characterization and properties of multiwalled carbon nanotubes from industrial waste as electromagnetic wave absorber. Journal of Nanoparticle Research, 24 (244). pp. 1-15. ISSN 1388-0764 (print), 1572-896X (online). (Published)
![[img]](http://umpir.ump.edu.my/style/images/fileicons/other.png) |
Pdf
Materials’ characterization and properties of multiwalled.pdf Restricted to Repository staff only Download (3MB) | Request a copy |
|
|
Pdf
Materials’ characterization and properties of multiwalled carbon nanotubes from industrial waste as electromagnetic wave absorber_ABS.pdf Download (261kB) | Preview |
Abstract
The development of high-frequency devices has attracted more research interest in electromagnetic wave–absorbing materials having lightweight, low filler content, thin thickness, minimum reflection loss and broad absorption bandwidth. Nevertheless, none of the materials uses steel waste (mill scale) as a potential low-cost catalyst to synthesize carbon nanotubes (CNT) as an electromagnetic (EM) wave absorber. Hence, multiwalled carbon nanotubes loaded in epoxy resin with an increasing polymer composite thickness of 1 mm, 2 mm, and 3 mm were introduced in this study. With varying milling times of mill scale (4 h, 20 h and 40 h) as catalyst, as-synthesized carbon nanotubes were produced using the chemical vapour deposition (CVD) method. Two main phases (carbon and iron carbide) were obtained from the synthesized carbon nanotubes. The samples’ morphology was mostly straight like, spiral, twisted carbon and spring pasta-like structures. The two-dimensional (2D) network structure of as-synthesized CNT loaded into epoxy resin, extends the transmission route of EM wave being absorbed. Moreover, the ratio of ID/IG is consistent at around 1.0 attributed to defective structure or a lower graphitization degree. In addition, higher electrical resistivity in the sample indicates wider separation between CNTs allowing for better EM wave absorption. The as-synthesized carbon nanotubes that are utilized as filler with lightweight properties, improved the reflection loss approach to − 25 dB (10.5 GHz) for growth CNT catalyzed by mill scale milled for 20 h loaded into polymer matrix (GM20h/P) at thickness of 3 mm. As the thickness of the polymer composites increased from 1 to 3 mm, all composite samples reflected a loss peak closer to a lower frequency range. The results demonstrated that the EM wave absorption ability was improved to 99.9% by using nanometer size mill scale waste as a catalyst to grow carbon nanotubes and further used as an EM wave absorber.
| Item Type: | Article |
|---|---|
| Additional Information: | Indexed by Scopus |
| Uncontrolled Keywords: | Absorbing materials; Carbon nanotubes; Filler; Mill scale; Nanometer; Nanostructured catalysts |
| Subjects: | H Social Sciences > HD Industries. Land use. Labor Q Science > Q Science (General) T Technology > T Technology (General) |
| Faculty/Division: | Faculty of Industrial Sciences And Technology |
| Depositing User: | Mr Muhamad Firdaus Janih@Jaini |
| Date Deposited: | 16 Apr 2024 04:26 |
| Last Modified: | 16 Apr 2024 04:26 |
| URI: | http://umpir.ump.edu.my/id/eprint/40436 |
| Download Statistic: | View Download Statistics |
Actions (login required)
 |
View Item |