N. A. A., Sathari and A. R., Razali and M., Ishak and L. H., Shah (2015) Mechanical Strength Of Dissimilar AA7075 and AA6061 Aluminum Alloys Using Friction Stir Welding. International Journal of Automotive and Mechanical Engineering (IJAME), 11. pp. 2713-2721. ISSN 1985-9325(Print); 2180-1606 (Online). (Published)
|
PDF
Mechanical Strength Of Dissimilar AA7075 and AA6061 Aluminum Alloys Using Friction Stir Welding.pdf - Published Version Available under License Creative Commons Attribution. Download (478kB) | Preview |
Abstract
The present study focuses on the effects of material position and tool rotational speed on the tensile strength of dissimilar AA7071 and AA6061 welded aluminum alloys with a thickness of 2.0 mm in using a conventional milling machine. Ten joints were produced by varying tool rotational speeds and by changing the fixed position of the material on the advancing and retreating sides. The results show that the maximum tensile strength of 207 MPa was achieved for Sample E when AA6061 aluminum alloys were placed on the advancing side at a rotational speed of 1000 rpm with seamless surface appearance and no inner defect across the weld area, while the lowest tensile strength of 160 MPa was obtained for Sample F when AA6061 was placed on the retreating side with severe tunnel defects across the weld area contributing to crack propagation. Thus, in dissimilar welding, weaker materials should be placed on the advancing side to trigger heat from the tool rotation and smooth the material flow formation in the stirred zone.
Item Type: | Article |
---|---|
Uncontrolled Keywords: | Friction stir welding; rotational speeds; aluminum alloys; tensile strength. |
Subjects: | T Technology > TJ Mechanical engineering and machinery |
Faculty/Division: | Faculty of Mechanical Engineering |
Depositing User: | Mrs. Neng Sury Sulaiman |
Date Deposited: | 07 Sep 2015 08:03 |
Last Modified: | 10 Jan 2018 03:16 |
URI: | http://umpir.ump.edu.my/id/eprint/9873 |
Download Statistic: | View Download Statistics |
Actions (login required)
View Item |