Rashidi, M. M. and Mohd Hasbullah, Idris (2014) The Effect Of Solidification On The Microstructure And Mechanical Properties Of Modified Ductile Ni-Resist Iron With A High Manganese Content. Materials Science and Engineering: A, 597. pp. 305-407. ISSN 0921-5093. (Published)
Full text not available from this repository.Abstract
In this study, ductile Ni-resist with a minimum of 18 wt. % nickel composition was modified. Up to 12 wt. % manganese was added together with 10 wt. % nickel to investigate the effects of the alloying elements on its solidification, microstructure and mechanical properties. Effect of solidification stage on the primary dendrite arm spacing (DAS), secondary dendrite arm spacing (SDAS), graphite aggregate, carbide and series of mechanical properties were evaluated. Results show that DAS, SDAS, graphite aggregate and carbide are directly dependent on the solidification-cooling rate. Consequently, a series of mechanical properties affected as well. A tensile strength of modified ductile Ni-resist is decrease with higher manganese content.
| Item Type: | Article |
|---|---|
| Subjects: | T Technology > TJ Mechanical engineering and machinery |
| Faculty/Division: | Faculty of Mechanical Engineering |
| Depositing User: | Ir Dr. Mohd Rashidi Maarof |
| Date Deposited: | 17 Dec 2014 06:33 |
| Last Modified: | 09 Jan 2015 08:40 |
| URI: | http://umpir.ump.edu.my/id/eprint/7851 |
| Download Statistic: | View Download Statistics |
Actions (login required)
 |
View Item |