Microstructure and high temperature oxidation of modified ductile ni-resist alloy with higher manganese content

Mohd Rashidi, Maarof and Mohd Hasbullah, Idris and Shayfull Zamree, Abd Rahim and Asnul Hadi, Ahmad and Mohd Mustafa Al Bakri, Abdullah and Pietrusiewicz, Paweł and Nabiałek, Marcin G. and Garus, J. (2022) Microstructure and high temperature oxidation of modified ductile ni-resist alloy with higher manganese content. Acta Physica Polonica A, 142 (1). pp. 56-59. ISSN 0587-4246. (Published)

[img] Pdf
Microstructure and high temperature oxidation of modified ductile.pdf
Restricted to Repository staff only

Download (606kB) | Request a copy
[img]
Preview
Pdf
Microstructure and high temperature oxidation of modified ductile ni-resist_ABS.pdf

Download (267kB) | Preview

Abstract

In this study, ductile Ni-resist with a minimum of 18 wt% nickel composition was modified. Up to 12 wt% manganese was added together with 10 wt% nickel to investigate the effects of the alloying elements on its microstructure, mechanical properties and isothermal oxidation behaviour. The results show a higher manganese composition on modified ductile Ni-resist with increased carbide formation, and a slightly decreased elevated temperature tensile strength. The addition of higher Mn [wt%] slightly increased the oxidation resistance. Three different oxide layers were observed on the modified ductile Ni-resist after 25 h hot corrosion at 765◦C.

Item Type: Article
Additional Information: Indexed by Scopus
Uncontrolled Keywords: High temperature oxidation; Manganese; Modified ductile; Topics: Ni-resist alloy
Subjects: T Technology > T Technology (General)
T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TJ Mechanical engineering and machinery
T Technology > TL Motor vehicles. Aeronautics. Astronautics
Faculty/Division: Faculty of Mechanical and Automotive Engineering Technology
Depositing User: Mr Muhamad Firdaus Janih@Jaini
Date Deposited: 22 Jan 2024 04:26
Last Modified: 22 Jan 2024 04:26
URI: http://umpir.ump.edu.my/id/eprint/40128
Download Statistic: View Download Statistics

Actions (login required)

View Item View Item