Megalingam, Arumugampillai and Asnul Hadi, Ahmad and Nasrul Azuan, Alang and Mohd Rashidi, Maarof and Naher, Sumsun Influence of processing parameters for globular microstructure formation of aluminium 7075 feedstock billet produced by direct thermal method. Journal of Advanced Manufacturing Technology. ISSN 1985-3157. (Published)
|
Pdf
Influence of processing parameters for globular microstructure.pdf Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (2MB) | Preview |
Abstract
This work aimed to evaluate the processing parameters for forming globular microstructures on billets of aluminium 7075 alloys with a direct thermal method (DTM). Semi-solid metal (SSM) processing is preferred to produce a high-quality product, which reduces casting flaws such as macroscopy, shrinkage, and porosity. It requires a solid globular microstructure in the semisolid aluminium liquid matrix. DTM is a simple SSM technique for creating a globular microstructure in a temperature environment that is typical of nature. In this experiment, molten aluminium 7075 alloys were poured into a cylindrical copper mould at pouring temperatures of 645 °C and 665 °C, then quenched into the water after holding times of 20, 40, and 60 s. Following that, the microstructure of feedstock billets prepared at a range of pouring temperatures and holding times was investigated. Limited information on aluminium 7075 alloy behaviour, and lack of proper understanding of globular microstructure formation are among the problems that arise in this research field. The influence of parameters on DTM processing should be investigated in detail. In particular, there is a lack of information about the aluminium 7075 effects near the liquidus temperature. Therefore, this study investigates the effects of globular microstructure formation and parameters in aluminium 7075 alloys in detail. A uniform high number of spherical primary particles is expected for a globular microstructure. The results of this experiment indicated that a pouring temperature of 665 °C combined with a holding time of 60 s produced a finer and globular microstructure.
| Item Type: | Article |
|---|---|
| Additional Information: | Indexed by Scopus |
| Uncontrolled Keywords: | Aluminium 7075 alloy; Direct thermal method; Feedstock billets; Holding time; Pouring temperature; Semisolid metal processing |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) T Technology > TJ Mechanical engineering and machinery T Technology > TN Mining engineering. Metallurgy |
| Faculty/Division: | Faculty of Mechanical and Automotive Engineering Technology |
| Depositing User: | Mrs. Nurul Hamira Abd Razak |
| Date Deposited: | 05 Jun 2025 01:39 |
| Last Modified: | 05 Jun 2025 01:39 |
| URI: | http://umpir.ump.edu.my/id/eprint/44723 |
| Download Statistic: | View Download Statistics |
Actions (login required)
 |
View Item |